Stainless Steel 205 1/4H vs 205-FH
Stainless Steel · 205 temper comparison
205 1/4H and 205-FH are two conditions of the same stainless steel grade, 205: 1/4H (quarter hard) versus FH (full hard). The chemistry is identical, so every difference below comes from the condition. 205-FH is the stronger of the two: yield strength 1,310 MPa (190 ksi) against 760 MPa (110 ksi) for 205 1/4H, about 72% more; tensile strength follows at 1,520 MPa (220 ksi) vs 1,035 MPa (150 ksi). In exchange, 205 1/4H is the more ductile: elongation 25% versus 8% for 205-FH, and 205-FH is harder (415 HV vs 285 HV). 205 1/4H runs hotter in service (800°C vs 300°C continuous). On the shop floor, 205 1/4H machines more easily (30 vs 20 out of 100).
205 1/4HChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
205-FHChoose it when strength drives the design.
205 1/4H vs 205-FH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 197 GPa28.6 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 475 MPa68.9 ksi · Fracture Toughness (K_IC) 180 MPa·√m164 ksi·√in · Hardness, Brinell 230 HB
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,385°C2,525 °F · Liquidus Temperature 1,425°C2,597 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14.5 W/m·K8.4 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.9 µm/m·K9.4 µin/in·°F · Latent Heat of Fusion 275 J/g118 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.3 % IACS · Electrical Resistivity 7.5×10⁻⁷ Ω·m29.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 48 MJ/kg20,636 BTU/lb · Embodied Carbon (primary production) 3.4 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
205 1/4H vs 205-FH — frequently asked
Is 205-FH stronger than 205 1/4H?
Yes. 205-FH has a typical yield strength of 1,310 MPa (190 ksi) against 760 MPa (110 ksi) for 205 1/4H — about 72% more. Tensile strength is 1,520 MPa (220 ksi) vs 1,035 MPa (150 ksi).
Which condition does FabDigit quote by default, 1/4H or FH?
ANN is the default 205 condition in the FabDigit quote flow (neither 1/4H nor FH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 205 1/4H or 205-FH?
205 1/4H, by a small margin. Both rate poor for machinability — 30/100 against 20/100 for 205-FH; for welding the order is 205 1/4H first (fair, 50/100) then 205-FH (fair, 42/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 205 1/4H and 205-FH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.