Stainless Steel 201L 1/4H vs 201L Annealed
Stainless Steel · 201L temper comparison
201L 1/4H and 201L Annealed are two conditions of the same stainless steel grade, 201L: 1/4H (quarter hard) versus Annealed. The chemistry is identical, so every difference below comes from the condition. 201L 1/4H is the stronger of the two: yield strength 570 MPa (82.7 ksi) against 370 MPa (53.7 ksi) for 201L Annealed, about 54% more; tensile strength follows at 900 MPa (131 ksi) vs 720 MPa (104 ksi). In exchange, 201L Annealed is the more ductile: elongation 52% versus 25% for 201L 1/4H, and 201L 1/4H is harder (275 HV vs 195 HV). 201L Annealed runs hotter in service (760°C vs 300°C continuous). On the shop floor, 201L Annealed welds better (very good vs good).
201L 1/4HChoose it when strength drives the design.
201L AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
201L 1/4H vs 201L Annealed: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 197 GPa28.6 Msi · Shear Modulus 76 GPa11 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 60% · Fracture Toughness (K_IC) 200 MPa·√m182 ksi·√in · Charpy V-Notch Impact (RT) 120 J88.5 ft·lbf · Hardness, Brinell 185 HB · Hardness, Rockwell B 90 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 16.2 W/m·K9.4 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15.7 µm/m·K8.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.5 % IACS · Electrical Resistivity 6.9×10⁻⁷ Ω·m27.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Machinability 38 / 100 · Brazeability / Solderability 65 / 100 · Polishability 78 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 45 MJ/kg19,347 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 90 L/kg10.8 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
201L 1/4H vs 201L Annealed — frequently asked
Is 201L 1/4H stronger than 201L Annealed?
Yes. 201L 1/4H has a typical yield strength of 570 MPa (82.7 ksi) against 370 MPa (53.7 ksi) for 201L Annealed — about 54% more. Tensile strength is 900 MPa (131 ksi) vs 720 MPa (104 ksi).
Which condition does FabDigit quote by default, 1/4H or Annealed?
Annealed is the default 201L condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 201L 1/4H or 201L Annealed?
201L Annealed. Its weldability rates very good (72/100) against good (62/100) for 201L 1/4H.