Stainless Steel 17-6PH-A vs 17-6PH-H1100
Stainless Steel · 17-6PH temper comparison
17-6PH-A and 17-6PH-H1100 are two conditions of the same stainless steel grade, 17-6PH: A (solution annealed) versus H1100 (aged 593 °C (1100 °F) for 4 h). The chemistry is identical, so every difference below comes from the condition. 17-6PH-H1100 is the stronger of the two: yield strength 900 MPa (131 ksi) against 760 MPa (110 ksi) for 17-6PH-A, about 18% more; tensile strength follows at 1,035 MPa (150 ksi) vs 965 MPa (140 ksi). 17-6PH-H1100 is the more ductile: elongation 15% versus 12% for 17-6PH-A, and 17-6PH-H1100 is harder (33 HRC vs 30 HRC). 17-6PH-H1100 runs hotter in service (400°C vs 300°C continuous).
17-6PH-H1100Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
17-6PH-A vs 17-6PH-H1100: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Shear Strength 620 MPa89.9 ksi · Hardness, Brinell 285 HB · Hardness, Vickers 300 HV
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 16 W/m·K9.2 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -75°C-103 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 56 MJ/kg24,076 BTU/lb · Embodied Carbon (primary production) 5 kg CO₂/kg · Embodied Water 210 L/kg25.2 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
17-6PH-A vs 17-6PH-H1100 — frequently asked
Is 17-6PH-H1100 stronger than 17-6PH-A?
Yes. 17-6PH-H1100 has a typical yield strength of 900 MPa (131 ksi) against 760 MPa (110 ksi) for 17-6PH-A — about 18% more. Tensile strength is 1,035 MPa (150 ksi) vs 965 MPa (140 ksi).
Which condition does FabDigit quote by default, A or H1100?
A is the default 17-6PH condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 17-6PH-A or 17-6PH-H1100?
17-6PH-A. Its machinability rates fair (38/100) against poor (33/100) for 17-6PH-H1100; for welding the order is 17-6PH-A first (fair, 45/100) then 17-6PH-H1100 (fair, 38/100).