Stainless Steel 1.4911 +A vs 1.4911 +QT1000
Stainless Steel · 1.4911 temper comparison
1.4911 +A and 1.4911 +QT1000 are two conditions of the same stainless steel grade, 1.4911: +A (annealed) versus +QT1000 (quenched and low-tempered, Rm ≈ 1000–1200 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4911 +QT1000 is the stronger of the two: yield strength 890 MPa (129 ksi) against 520 MPa (75.4 ksi) for 1.4911 +A, about 71% more; tensile strength follows at 1,090 MPa (158 ksi) vs 780 MPa (113 ksi). In exchange, 1.4911 +A is the more ductile: elongation 20% versus 13% for 1.4911 +QT1000, and 1.4911 +QT1000 is harder (330 HB vs 240 HB). 1.4911 +QT1000 runs hotter in service (550°C vs 450°C continuous). On the shop floor, 1.4911 +A machines more easily (fair vs poor).
1.4911 +AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4911 +QT1000Choose it when strength drives the design, or when the part sees heat.
1.4911 +A vs 1.4911 +QT1000: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 216 GPa31.3 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29 · Compressive Strength 790 MPa115 ksi · Shear Strength 590 MPa85.6 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.78 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24 W/m·K13.9 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 265 J/g114 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V · Corrosion Resistance 35 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 32 / 100 · Castability 40 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4911 +A vs 1.4911 +QT1000 — frequently asked
Is 1.4911 +QT1000 stronger than 1.4911 +A?
Yes. 1.4911 +QT1000 has a typical yield strength of 890 MPa (129 ksi) against 520 MPa (75.4 ksi) for 1.4911 +A — about 71% more. Tensile strength is 1,090 MPa (158 ksi) vs 780 MPa (113 ksi).
Which condition does FabDigit quote by default, +A or +QT1000?
+QT900 is the default 1.4911 condition in the FabDigit quote flow (neither +A nor +QT1000). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4911 +A or 1.4911 +QT1000?
1.4911 +A. Its machinability rates fair (40/100) against poor (26/100) for 1.4911 +QT1000.