Stainless Steel 1.4877 vs 2205
Stainless Steel · grade comparison
Stainless Steel 1.4877 and 2205 are both stainless steel grades. 2205 is the stronger of the two: yield strength 540 MPa (78.3 ksi) against 260 MPa (37.7 ksi) for 1.4877, about 108% more; tensile strength follows at 790 MPa (115 ksi) vs 600 MPa (87 ksi). In exchange, 1.4877 is the more ductile: elongation 40% versus 30% for 2205, and 2205 is harder (255 HB vs 170 HB). 1.4877 runs hotter in service (1,100°C vs 300°C continuous) and 2205 conducts heat better (16 W/m·K vs 11.5 W/m·K). On the shop floor, 2205 welds better (very good vs good) and 1.4877 sits in a lower cost tier (high, $$$$) than 2205 (specialty, $$$$$).
1.4877Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
2205Choose it when strength drives the design, or when it will be welded.
1.4877 vs 2205: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Fracture Toughness (K_IC)
Hardness, Rockwell C
Same in both: Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4877 | 2205 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Solution Annealed |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | 1 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Passivation (Stainless Steel) | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4877 vs 2205 — frequently asked
Is 2205 stronger than 1.4877?
Yes. 2205 has a typical yield strength of 540 MPa (78.3 ksi) against 260 MPa (37.7 ksi) for 1.4877 — about 108% more. Tensile strength is 790 MPa (115 ksi) vs 600 MPa (87 ksi).
Which is cheaper, 1.4877 or 2205?
1.4877 is the lower-cost material: it sits in the high tier ($$$$) while 2205 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4877 or 2205?
2205, by a small margin. Both rate poor for machinability — 32/100 against 25/100 for 1.4877; for welding the order is 2205 first (very good, 78/100) then 1.4877 (good, 68/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4877 and 2205 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.