Stainless Steel 1.4849 vs CK3MCuN
Stainless Steel · grade comparison
Stainless Steel 1.4849 and CK3MCuN are both stainless steel grades. CK3MCuN is the stronger of the two: yield strength 295 MPa (42.8 ksi) against 250 MPa (36.3 ksi) for 1.4849, about 18% more; tensile strength follows at 585 MPa (84.8 ksi) vs 490 MPa (71.1 ksi). CK3MCuN is the more ductile: elongation 45% versus 10% for 1.4849. CK3MCuN is stiffer (195 GPa vs 170 GPa) and 1.4849 runs hotter in service (1,050°C vs 400°C continuous). On the shop floor, CK3MCuN welds better (very good vs good).
1.4849Choose it when the part sees heat.
CK3MCuNChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1.4849 vs CK3MCuN: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 1,320°C2,408 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Conductivity 13.5 W/m·K7.8 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 3.4 mm²/s
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4849 | CK3MCuN |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4849 vs CK3MCuN — frequently asked
Is CK3MCuN stronger than 1.4849?
Yes. CK3MCuN has a typical yield strength of 295 MPa (42.8 ksi) against 250 MPa (36.3 ksi) for 1.4849 — about 18% more. Tensile strength is 585 MPa (84.8 ksi) vs 490 MPa (71.1 ksi).
Which is cheaper, 1.4849 or CK3MCuN?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4849 or CK3MCuN?
CK3MCuN, by a small margin. Both rate poor for machinability — 25/100 against 20/100 for 1.4849; for welding the order is CK3MCuN first (very good, 70/100) then 1.4849 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4849 and CK3MCuN side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.