Stainless Steel 1.4308 vs 1.4849
Stainless Steel · grade comparison
Stainless Steel 1.4308 and 1.4849 are both stainless steel grades. 1.4308 is the stronger of the two: tensile strength 520 MPa (75.4 ksi) against 490 MPa (71.1 ksi) for 1.4849, about 6% more. 1.4308 is the more ductile: elongation 50% versus 10% for 1.4849, and 1.4849 is harder (180 HB vs 140 HB). 1.4308 is stiffer (195 GPa vs 170 GPa) and 1.4849 runs hotter in service (1,050°C vs 760°C continuous). On the shop floor, 1.4308 machines more easily (fair vs poor), 1.4308 welds better (excellent vs good), and 1.4308 sits in a lower cost tier (premium, $$$) than 1.4849 (high, $$$$).
1.4308Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1.4849Choose it when the part sees heat.
1.4308 vs 1.4849: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.29 · Yield Strength (0.2% offset) 250 MPa36.3 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 70%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4308 | 1.4849 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4308 vs 1.4849 — frequently asked
Is 1.4308 stronger than 1.4849?
Yes. 1.4308 has a typical tensile strength of 520 MPa (75.4 ksi) against 490 MPa (71.1 ksi) for 1.4849 — about 6% more.
Which is cheaper, 1.4308 or 1.4849?
1.4308 is the lower-cost material: it sits in the premium tier ($$$) while 1.4849 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4308 or 1.4849?
1.4308. Its machinability rates fair (40/100) against poor (20/100) for 1.4849; for welding the order is 1.4308 first (excellent, 88/100) then 1.4849 (good, 55/100).