Stainless Steel 1.4837 vs CF8C
Stainless Steel · grade comparison
Stainless Steel 1.4837 and CF8C are both stainless steel grades. Both yield at about 265 MPa — strength does not separate them. CF8C is the more ductile: elongation 39% versus 12% for 1.4837, and 1.4837 is harder (190 HB vs 150 HB). 1.4837 runs hotter in service (1,050°C vs 816°C continuous) and CF8C conducts heat better (16.3 W/m·K vs 14.5 W/m·K). On the shop floor, CF8C machines more easily (fair vs poor) and CF8C welds better (excellent vs fair).
1.4837Choose it when the part sees heat.
CF8CChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4837 vs CF8C: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Fracture Toughness (K_IC)
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Brazeability / Solderability
Same in both: Castability 72 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 70%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4837 | CF8C |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4837 vs CF8C — frequently asked
What is the difference between 1.4837 and CF8C?
Stainless Steel 1.4837 and CF8C are both stainless steel grades. Both yield at about 265 MPa — strength does not separate them. CF8C is the more ductile: elongation 39% versus 12% for 1.4837, and 1.4837 is harder (190 HB vs 150 HB).
Which is cheaper, 1.4837 or CF8C?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4837 or CF8C?
CF8C. Its machinability rates fair (40/100) against poor (22/100) for 1.4837; for welding the order is CF8C first (excellent, 85/100) then 1.4837 (fair, 40/100).