Stainless Steel 1.4837 vs CF16F
Stainless Steel · grade comparison
Stainless Steel 1.4837 and CF16F are both stainless steel grades. 1.4837 is the stronger of the two: yield strength 265 MPa (38.4 ksi) against 240 MPa (34.8 ksi) for CF16F, about 10% more. In exchange, CF16F is the more ductile: elongation 38% versus 12% for 1.4837, and 1.4837 is harder (190 HB vs 150 HB). 1.4837 runs hotter in service (1,050°C vs 650°C continuous) and CF16F conducts heat better (16.2 W/m·K vs 14.5 W/m·K). On the shop floor, CF16F machines more easily (good vs poor) and 1.4837 welds better (fair vs poor).
1.4837Choose it when strength drives the design, or when the part sees heat.
CF16FChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4837 vs CF16F: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Fracture Toughness (K_IC)
Same in both: Poisson's Ratio 0.29 · Fatigue Strength (Endurance Limit) 200 MPa29 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Polishability
Brazeability / Solderability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4837 | CF16F |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4837 vs CF16F — frequently asked
Is 1.4837 stronger than CF16F?
Yes. 1.4837 has a typical yield strength of 265 MPa (38.4 ksi) against 240 MPa (34.8 ksi) for CF16F — about 10% more. Tensile strength is 520 MPa (75.4 ksi) vs 505 MPa (73.2 ksi).
Which is cheaper, 1.4837 or CF16F?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4837 or CF16F?
CF16F. Its machinability rates good (55/100) against poor (22/100) for 1.4837; for welding the order is 1.4837 first (fair, 40/100) then CF16F (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4837 and CF16F side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.