Stainless Steel 1.4837 vs CF10SMnN
Stainless Steel · grade comparison
Stainless Steel 1.4837 and CF10SMnN are both stainless steel grades. CF10SMnN is the stronger of the two: yield strength 330 MPa (47.9 ksi) against 265 MPa (38.4 ksi) for 1.4837, about 25% more; tensile strength follows at 640 MPa (92.8 ksi) vs 520 MPa (75.4 ksi). CF10SMnN is the more ductile: elongation 42% versus 12% for 1.4837. CF10SMnN is stiffer (196 GPa vs 185 GPa) and 1.4837 runs hotter in service (1,050°C vs 870°C continuous). On the shop floor, CF10SMnN welds better (very good vs fair) and 1.4837 sits in a lower cost tier (premium, $$$) than CF10SMnN (high, $$$$).
1.4837Choose it when the part sees heat, or when cost is the deciding factor.
CF10SMnNChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1.4837 vs CF10SMnN: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Fracture Toughness (K_IC)
Same in both: Hardness, Brinell 190 HB · Hardness, Rockwell B 92 HRB
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 1,370°C2,498 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Polishability
Brazeability / Solderability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 70%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4837 | CF10SMnN |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4837 vs CF10SMnN — frequently asked
Is CF10SMnN stronger than 1.4837?
Yes. CF10SMnN has a typical yield strength of 330 MPa (47.9 ksi) against 265 MPa (38.4 ksi) for 1.4837 — about 25% more. Tensile strength is 640 MPa (92.8 ksi) vs 520 MPa (75.4 ksi).
Which is cheaper, 1.4837 or CF10SMnN?
1.4837 is the lower-cost material: it sits in the premium tier ($$$) while CF10SMnN is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 1.4837 or CF10SMnN?
CF10SMnN. Its weldability rates very good (70/100) against fair (40/100) for 1.4837.