Stainless Steel 1.4634 vs 409
Stainless Steel · grade comparison
Stainless Steel 1.4634 and 409 are both stainless steel grades. 1.4634 is the stronger of the two: yield strength 310 MPa (45 ksi) against 250 MPa (36.3 ksi) for 409, about 24% more; tensile strength follows at 480 MPa (69.6 ksi) vs 450 MPa (65.3 ksi). In exchange, 409 is the more ductile: elongation 30% versus 26% for 1.4634, and 1.4634 is harder (170 HB vs 150 HB). 1.4634 is stiffer (220 GPa vs 200 GPa) and 1.4634 runs hotter in service (950°C vs 675°C continuous). On the shop floor, 409 machines more easily (good vs fair), 409 welds better (80 vs 70 out of 100), and 1.4634 sits in a lower cost tier (standard, $$) than 409 (premium, $$$).
1.4634Choose it when strength drives the design, or when the part sees heat.
409Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4634 vs 409: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Reduction in Area
Compressive Strength
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.7 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Embodied Water 90 L/kg10.8 gal/lb · Typical Recycled Content 65%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 5
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4634 | 409 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Passivation (Stainless Steel) | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4634 vs 409 — frequently asked
Is 1.4634 stronger than 409?
Yes. 1.4634 has a typical yield strength of 310 MPa (45 ksi) against 250 MPa (36.3 ksi) for 409 — about 24% more. Tensile strength is 480 MPa (69.6 ksi) vs 450 MPa (65.3 ksi).
Which is cheaper, 1.4634 or 409?
1.4634 is the lower-cost material: it sits in the standard tier ($$) while 409 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4634 or 409?
409. Its machinability rates good (55/100) against fair (42/100) for 1.4634; for welding the order is 409 first (very good, 80/100) then 1.4634 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4634 and 409 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.