Stainless Steel 1.4596 +AT vs 1.4596 +P1400
Stainless Steel · 1.4596 temper comparison
1.4596 +AT and 1.4596 +P1400 are two conditions of the same stainless steel grade, 1.4596: +AT (solution annealed) versus +P1400 (precipitation hardened, Rm ≥ 1400 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4596 +P1400 is the stronger of the two: yield strength 1,350 MPa (196 ksi) against 750 MPa (109 ksi) for 1.4596 +AT, about 80% more; tensile strength follows at 1,470 MPa (213 ksi) vs 950 MPa (138 ksi). In exchange, 1.4596 +AT is the more ductile: elongation 18% versus 12% for 1.4596 +P1400, and 1.4596 +P1400 is harder (430 HB vs 290 HB). 1.4596 +P1400 runs hotter in service (400°C vs 350°C continuous). On the shop floor, 1.4596 +AT machines more easily (fair vs poor) and 1.4596 +AT welds better (very good vs good).
1.4596 +ATChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4596 +P1400Choose it when strength drives the design, or when the part sees heat.
1.4596 +AT vs 1.4596 +P1400: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 16 W/m·K9.2 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.9 % IACS · Electrical Resistivity 9×10⁻⁷ Ω·m35.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 70 MJ/kg30,095 BTU/lb · Embodied Carbon (primary production) 5.6 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4596 +AT vs 1.4596 +P1400 — frequently asked
Is 1.4596 +P1400 stronger than 1.4596 +AT?
Yes. 1.4596 +P1400 has a typical yield strength of 1,350 MPa (196 ksi) against 750 MPa (109 ksi) for 1.4596 +AT — about 80% more. Tensile strength is 1,470 MPa (213 ksi) vs 950 MPa (138 ksi).
Which condition does FabDigit quote by default, +AT or +P1400?
+P1400 is the default 1.4596 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4596 +AT or 1.4596 +P1400?
1.4596 +AT. Its machinability rates fair (40/100) against poor (30/100) for 1.4596 +P1400; for welding the order is 1.4596 +AT first (very good, 70/100) then 1.4596 +P1400 (good, 60/100).