Stainless Steel 1.4594-H900 vs 1.4594 +P1070
Stainless Steel · 1.4594 temper comparison
1.4594-H900 and 1.4594 +P1070 are two conditions of the same stainless steel grade, 1.4594: H900 (aged 482 °C (900 °F) for 1 h, peak hardness) versus +P1070 (precipitation hardened, Rm ≥ 1070 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4594-H900 is the stronger of the two: yield strength 1,240 MPa (180 ksi) against 1,010 MPa (146 ksi) for 1.4594 +P1070, about 23% more; tensile strength follows at 1,310 MPa (190 ksi) vs 1,100 MPa (160 ksi). In exchange, 1.4594 +P1070 is the more ductile: elongation 15% versus 13% for 1.4594-H900, and 1.4594-H900 is harder (390 HB vs 330 HB). 1.4594 +P1070 runs hotter in service (350°C vs 300°C continuous).
1.4594-H900Choose it when strength drives the design.
1.4594 +P1070Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4594-H900 vs 1.4594 +P1070: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 800 MPa116 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,440°C2,624 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 17 W/m·K9.8 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.6 µm/m·K5.9 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 70 / 100 · Formability (cold) 45 / 100 · Brazeability / Solderability 45 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4594-H900 vs 1.4594 +P1070 — frequently asked
Is 1.4594-H900 stronger than 1.4594 +P1070?
Yes. 1.4594-H900 has a typical yield strength of 1,240 MPa (180 ksi) against 1,010 MPa (146 ksi) for 1.4594 +P1070 — about 23% more. Tensile strength is 1,310 MPa (190 ksi) vs 1,100 MPa (160 ksi).
Which condition does FabDigit quote by default, H900 or +P1070?
+AT is the default 1.4594 condition in the FabDigit quote flow (neither H900 nor +P1070). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4594-H900 or 1.4594 +P1070?
1.4594 +P1070. Its machinability rates fair (36/100) against poor (28/100) for 1.4594-H900.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4594-H900 and 1.4594 +P1070 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.