Stainless Steel 1.4584 vs 1.4849
Stainless Steel · grade comparison
Stainless Steel 1.4584 and 1.4849 are both stainless steel grades. 1.4849 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 230 MPa (33.4 ksi) for 1.4584, about 9% more. In exchange, 1.4584 is the more ductile: elongation 40% versus 10% for 1.4849, and 1.4849 is harder (180 HB vs 160 HB). 1.4584 is stiffer (190 GPa vs 170 GPa) and 1.4849 runs hotter in service (1,050°C vs 400°C continuous). On the shop floor, 1.4584 machines more easily (30 vs 20 out of 100) and 1.4584 welds better (very good vs good).
1.4584Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4849Choose it when strength drives the design, or when the part sees heat.
1.4584 vs 1.4849: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Tensile Strength (Ultimate) 490 MPa71.1 ksi · Fatigue Strength (Endurance Limit) 190 MPa27.6 ksi
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 1,320°C2,408 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.7 % IACS · Electrical Resistivity 1×10⁻⁶ Ω·m39.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4584 | 1.4849 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4584 vs 1.4849 — frequently asked
Is 1.4849 stronger than 1.4584?
Yes. 1.4849 has a typical yield strength of 250 MPa (36.3 ksi) against 230 MPa (33.4 ksi) for 1.4584 — about 9% more. Tensile strength is 490 MPa (71.1 ksi) vs 490 MPa (71.1 ksi).
Which is cheaper, 1.4584 or 1.4849?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4584 or 1.4849?
1.4584, by a small margin. Both rate poor for machinability — 30/100 against 20/100 for 1.4849; for welding the order is 1.4584 first (very good, 75/100) then 1.4849 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4584 and 1.4849 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.