Stainless Steel 1.4317 vs CA28MWV
Stainless Steel · grade comparison
Stainless Steel 1.4317 and CA28MWV are both stainless steel grades. CA28MWV is the stronger of the two: yield strength 760 MPa (110 ksi) against 620 MPa (89.9 ksi) for 1.4317, about 23% more; tensile strength follows at 1,035 MPa (150 ksi) vs 830 MPa (120 ksi). In exchange, 1.4317 is the more ductile: elongation 18% versus 13% for CA28MWV, and CA28MWV is harder (302 HB vs 260 HB). CA28MWV runs hotter in service (593°C vs 450°C continuous). On the shop floor, 1.4317 machines more easily (fair vs poor) and 1.4317 welds better (very good vs poor).
1.4317Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
CA28MWVChoose it when strength drives the design, or when the part sees heat.
1.4317 vs CA28MWV: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4317 | CA28MWV |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4317 vs CA28MWV — frequently asked
Is CA28MWV stronger than 1.4317?
Yes. CA28MWV has a typical yield strength of 760 MPa (110 ksi) against 620 MPa (89.9 ksi) for 1.4317 — about 23% more. Tensile strength is 1,035 MPa (150 ksi) vs 830 MPa (120 ksi).
Which is cheaper, 1.4317 or CA28MWV?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4317 or CA28MWV?
1.4317. Its machinability rates fair (40/100) against poor (30/100) for CA28MWV; for welding the order is 1.4317 first (very good, 70/100) then CA28MWV (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4317 and CA28MWV side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.