Stainless Steel 1.4307 +AT vs 1.4307 +C700
Stainless Steel · 1.4307 temper comparison
1.4307 +AT and 1.4307 +C700 are two conditions of the same stainless steel grade, 1.4307: +AT (solution annealed) versus +C700 (cold worked to tensile strength class 700 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4307 +C700 is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 290 MPa (42.1 ksi) for 1.4307 +AT, about 79% more; tensile strength follows at 760 MPa (110 ksi) vs 580 MPa (84.1 ksi). In exchange, 1.4307 +AT is the more ductile: elongation 55% versus 25% for 1.4307 +C700, and 1.4307 +C700 is harder (230 HB vs 150 HB). 1.4307 +AT runs hotter in service (425°C vs 300°C continuous). On the shop floor, 1.4307 +C700 machines more easily (50 vs 38 out of 100) and 1.4307 +AT welds better (95 vs 85 out of 100).
1.4307 +ATChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4307 +C700Choose it when strength drives the design, or when the part is machined in volume.
1.4307 +AT vs 1.4307 +C700: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.29 · Compressive Strength 290 MPa42.1 ksi · Fracture Toughness (K_IC) 200 MPa·√m182 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.9 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16 µm/m·K8.9 µin/in·°F · Latent Heat of Fusion 285 J/g123 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.4 % IACS · Electrical Resistivity 7.2×10⁻⁷ Ω·m28.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 65 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4307 +AT vs 1.4307 +C700 — frequently asked
Is 1.4307 +C700 stronger than 1.4307 +AT?
Yes. 1.4307 +C700 has a typical yield strength of 520 MPa (75.4 ksi) against 290 MPa (42.1 ksi) for 1.4307 +AT — about 79% more. Tensile strength is 760 MPa (110 ksi) vs 580 MPa (84.1 ksi).
Which condition does FabDigit quote by default, +AT or +C700?
+AT is the default 1.4307 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4307 +AT or 1.4307 +C700?
1.4307 +C700, by a small margin. Both rate fair for machinability — 50/100 against 38/100 for 1.4307 +AT; for welding the order is 1.4307 +AT first (excellent, 95/100) then 1.4307 +C700 (excellent, 85/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4307 +AT and 1.4307 +C700 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.