Stainless Steel 1.4035 +C vs 1.4035 +QT700
Stainless Steel · 1.4035 temper comparison
1.4035 +C and 1.4035 +QT700 are two conditions of the same stainless steel grade, 1.4035: +C (cold drawn) versus +QT700 (quenched and tempered, Rm 700–850 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4035 +C is the stronger of the two: yield strength 650 MPa (94.3 ksi) against 560 MPa (81.2 ksi) for 1.4035 +QT700, about 16% more; tensile strength follows at 850 MPa (123 ksi) vs 780 MPa (113 ksi). In exchange, 1.4035 +QT700 is the more ductile: elongation 12% versus 8% for 1.4035 +C, and 1.4035 +C is harder (260 HB vs 240 HB). 1.4035 +QT700 runs hotter in service (400°C vs 300°C continuous). On the shop floor, 1.4035 +C machines more easily (very good vs good).
1.4035 +CChoose it when strength drives the design, or when the part is machined in volume.
1.4035 +QT700Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4035 +C vs 1.4035 +QT700: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 215 GPa31.2 Msi · Shear Modulus 82 GPa11.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Fatigue Strength (Endurance Limit) 350 MPa50.8 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 30 W/m·K17.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.35 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 12 / 100 · Brazeability / Solderability 40 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 52 MJ/kg22,356 BTU/lb · Embodied Carbon (primary production) 4.3 kg CO₂/kg · Embodied Water 190 L/kg22.8 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4035 +C vs 1.4035 +QT700 — frequently asked
Is 1.4035 +C stronger than 1.4035 +QT700?
Yes. 1.4035 +C has a typical yield strength of 650 MPa (94.3 ksi) against 560 MPa (81.2 ksi) for 1.4035 +QT700 — about 16% more. Tensile strength is 850 MPa (123 ksi) vs 780 MPa (113 ksi).
Which condition does FabDigit quote by default, +C or +QT700?
+A is the default 1.4035 condition in the FabDigit quote flow (neither +C nor +QT700). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4035 +C or 1.4035 +QT700?
1.4035 +C. Its machinability rates very good (72/100) against good (58/100) for 1.4035 +QT700.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4035 +C and 1.4035 +QT700 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.