Refractory Metal Zr 704 Annealed vs Zr 704 CW-SR
Refractory Metal · Zr 704 temper comparison
Zr 704 Annealed and Zr 704 CW-SR are two conditions of the same refractory metal grade, Zr 704: Annealed versus CW-SR (cold Worked and Stress Relieved). The chemistry is identical, so every difference below comes from the condition. Zr 704 CW-SR is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 300 MPa (43.5 ksi) for Zr 704 Annealed, about 60% more; tensile strength follows at 600 MPa (87 ksi) vs 470 MPa (68.2 ksi). In exchange, Zr 704 Annealed is the more ductile: elongation 22% versus 14% for Zr 704 CW-SR, and Zr 704 CW-SR is harder (222 HB vs 180 HB). Zr 704 Annealed runs hotter in service (400°C vs 350°C continuous). On the shop floor, Zr 704 Annealed welds better (80 vs 70 out of 100).
Zr 704 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Zr 704 CW-SRChoose it when strength drives the design.
Zr 704 Annealed vs Zr 704 CW-SR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 99 GPa14.4 Msi · Shear Modulus 36 GPa5.2 Msi · Bulk Modulus 100 GPa14.5 Msi · Poisson's Ratio 0.35
Physical
Density and transition temperatures.
Same in both: Density 6.57 g/cm³0.24 lb/in³ · Melting Point (Solidus) 1,840°C3,344 °F · Liquidus Temperature 1,855°C3,371 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14.6 W/m·K8.4 BTU/hr·ft·°F · Specific Heat Capacity 285 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 6 µm/m·K3.3 µin/in·°F · Latent Heat of Fusion 210 J/g90.3 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 20 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,400 MJ/kg601,892 BTU/lb · Embodied Carbon (primary production) 95 kg CO₂/kg · Embodied Water 900 L/kg108 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every refractory metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Zr 704 Annealed vs Zr 704 CW-SR — frequently asked
Is Zr 704 CW-SR stronger than Zr 704 Annealed?
Yes. Zr 704 CW-SR has a typical yield strength of 480 MPa (69.6 ksi) against 300 MPa (43.5 ksi) for Zr 704 Annealed — about 60% more. Tensile strength is 600 MPa (87 ksi) vs 470 MPa (68.2 ksi).
Which condition does FabDigit quote by default, Annealed or CW-SR?
Annealed is the default Zr 704 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, Zr 704 Annealed or Zr 704 CW-SR?
Zr 704 CW-SR. Its machinability rates fair (35/100) against poor (30/100) for Zr 704 Annealed; for welding the order is Zr 704 Annealed first (very good, 80/100) then Zr 704 CW-SR (very good, 70/100).