Refractory Metal Zr 704 Annealed vs Zr 704-AW
Refractory Metal · Zr 704 temper comparison
Zr 704 Annealed and Zr 704-AW are two conditions of the same refractory metal grade, Zr 704: Annealed versus AW (as-welded deposit). The chemistry is identical, so every difference below comes from the condition. Both yield at about 300 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (Annealed versus as-welded deposit). Zr 704 Annealed is the more ductile: elongation 22% versus 14% for Zr 704-AW, and Zr 704-AW is harder (192 HB vs 180 HB).
Zr 704 AnnealedChoose it when the part is bent, formed or impact-loaded.
Zr 704 Annealed vs Zr 704-AW: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 99 GPa14.4 Msi · Shear Modulus 36 GPa5.2 Msi · Bulk Modulus 100 GPa14.5 Msi · Poisson's Ratio 0.35 · Yield Strength (0.2% offset) 300 MPa43.5 ksi · Compressive Strength 310 MPa45 ksi
Physical
Density and transition temperatures.
Same in both: Density 6.57 g/cm³0.24 lb/in³ · Melting Point (Solidus) 1,840°C3,344 °F · Liquidus Temperature 1,855°C3,371 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 14.6 W/m·K8.4 BTU/hr·ft·°F · Specific Heat Capacity 285 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 6 µm/m·K3.3 µin/in·°F · Latent Heat of Fusion 210 J/g90.3 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 3.4 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 20 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,400 MJ/kg601,892 BTU/lb · Embodied Carbon (primary production) 95 kg CO₂/kg · Embodied Water 900 L/kg108 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every refractory metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Zr 704 Annealed vs Zr 704-AW — frequently asked
What is the difference between Zr 704 Annealed and Zr 704-AW?
Zr 704 Annealed and Zr 704-AW are two conditions of the same refractory metal grade, Zr 704: Annealed versus AW (as-welded deposit). The chemistry is identical, so every difference below comes from the condition. Both yield at about 300 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (Annealed versus as-welded deposit).
Which condition does FabDigit quote by default, Annealed or AW?
Annealed is the default Zr 704 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Zr 704 Annealed or Zr 704-AW?
Zr 704 Annealed. Its weldability rates very good (80/100) against very good (75/100) for Zr 704-AW.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Zr 704 Annealed and Zr 704-AW side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.