Refractory Metal 60Cr-40Ni vs FeCr-LC
Refractory Metal · grade comparison
Refractory Metal 60Cr-40Ni and FeCr-LC are both refractory metal grades. 60Cr-40Ni is the stronger of the two: tensile strength 415 MPa (60.2 ksi) against 200 MPa (29 ksi) for FeCr-LC, about 108% more. 60Cr-40Ni is the more ductile: elongation 2% versus 0.1% for FeCr-LC, and FeCr-LC is harder (455 HB vs 220 HB). FeCr-LC is lighter (7.2 g/cm³ vs 7.7 g/cm³ for 60Cr-40Ni) and 60Cr-40Ni runs hotter in service (1,150°C vs 850°C continuous). On the shop floor, 60Cr-40Ni welds better (poor vs not recommended) and FeCr-LC sits in a lower cost tier (budget, $) than 60Cr-40Ni (high, $$$$).
60Cr-40NiChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
FeCr-LCChoose it when weight is the constraint, or when cost is the deciding factor.
60Cr-40Ni vs FeCr-LC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Latent Heat of Fusion
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 2
Strength versus weight
Yield strength against density for every refractory metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 60Cr-40Ni | FeCr-LC |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
60Cr-40Ni vs FeCr-LC — frequently asked
Is 60Cr-40Ni stronger than FeCr-LC?
Yes. 60Cr-40Ni has a typical tensile strength of 415 MPa (60.2 ksi) against 200 MPa (29 ksi) for FeCr-LC — about 108% more.
Which is cheaper, 60Cr-40Ni or FeCr-LC?
FeCr-LC is the lower-cost material: it sits in the budget tier ($) while 60Cr-40Ni is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 60Cr-40Ni or FeCr-LC?
60Cr-40Ni, by a small margin. Both rate not recommended for machinability — 12/100 against 3/100 for FeCr-LC; for welding the order is 60Cr-40Ni first (poor, 20/100) then FeCr-LC (not recommended, 5/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 60Cr-40Ni and FeCr-LC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.