Precious Metal PdRu5 Annealed vs PdRu5-H02
Precious Metal · PdRu5 temper comparison
PdRu5 Annealed and PdRu5-H02 are two conditions of the same precious metal grade, PdRu5: Annealed versus H02 (half hard). The chemistry is identical, so every difference below comes from the condition. PdRu5-H02 is the stronger of the two: yield strength 600 MPa (87 ksi) against 210 MPa (30.5 ksi) for PdRu5 Annealed, about 186% more; tensile strength follows at 720 MPa (104 ksi) vs 450 MPa (65.3 ksi). In exchange, PdRu5 Annealed is the more ductile: elongation 25% versus 6% for PdRu5-H02, and PdRu5-H02 is harder (180 HB vs 114 HB). PdRu5 Annealed runs hotter in service (500°C vs 400°C continuous). On the shop floor, PdRu5-H02 machines more easily (fair vs poor) and PdRu5 Annealed welds better (very good vs good).
PdRu5 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
PdRu5-H02Choose it when strength drives the design, or when the part is machined in volume.
PdRu5 Annealed vs PdRu5-H02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 50 GPa7.3 Msi · Bulk Modulus 195 GPa28.3 Msi · Poisson's Ratio 0.39
Physical
Density and transition temperatures.
Same in both: Density 12.05 g/cm³0.44 lb/in³ · Melting Point (Solidus) 1,575°C2,867 °F · Liquidus Temperature 1,600°C2,912 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 245 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 157 J/g67.5 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.2 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 80 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 95,000 MJ/kg4.08×10⁷ BTU/lb · Embodied Carbon (primary production) 3,800 kg CO₂/kg · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PdRu5 Annealed vs PdRu5-H02 — frequently asked
Is PdRu5-H02 stronger than PdRu5 Annealed?
Yes. PdRu5-H02 has a typical yield strength of 600 MPa (87 ksi) against 210 MPa (30.5 ksi) for PdRu5 Annealed — about 186% more. Tensile strength is 720 MPa (104 ksi) vs 450 MPa (65.3 ksi).
Which condition does FabDigit quote by default, Annealed or H02?
Annealed is the default PdRu5 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, PdRu5 Annealed or PdRu5-H02?
PdRu5-H02. Its machinability rates fair (35/100) against poor (25/100) for PdRu5 Annealed; for welding the order is PdRu5 Annealed first (very good, 70/100) then PdRu5-H02 (good, 55/100).