Precious Metal PdNi-F vs PdNi-H02
Precious Metal · PdNi temper comparison
PdNi-F and PdNi-H02 are two conditions of the same precious metal grade, PdNi: F (as fabricated) versus H02 (half hard). The chemistry is identical, so every difference below comes from the condition. PdNi-H02 is the stronger of the two: yield strength 600 MPa (87 ksi) against 220 MPa (31.9 ksi) for PdNi-F, about 173% more; tensile strength follows at 750 MPa (109 ksi) vs 450 MPa (65.3 ksi). In exchange, PdNi-F is the more ductile: elongation 15% versus 8% for PdNi-H02, and PdNi-H02 is harder (200 HB vs 124 HB). PdNi-F runs hotter in service (600°C vs 400°C continuous). On the shop floor, PdNi-H02 machines more easily (fair vs poor).
PdNi-FChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
PdNi-H02Choose it when strength drives the design, or when the part is machined in volume.
PdNi-F vs PdNi-H02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 53 GPa7.7 Msi · Bulk Modulus 185 GPa26.8 Msi · Poisson's Ratio 0.35
Physical
Density and transition temperatures.
Same in both: Density 11.3 g/cm³0.41 lb/in³ · Melting Point (Solidus) 1,275°C2,327 °F · Liquidus Temperature 1,305°C2,381 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24 W/m·K13.9 BTU/hr·ft·°F · Specific Heat Capacity 285 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 185 J/g79.5 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 5 % IACS · Electrical Resistivity 3.45×10⁻⁷ Ω·m13.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0.2 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Castability
Same in both: Weldability 55 / 100 · Brazeability / Solderability 80 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58,000 MJ/kg2.49×10⁷ BTU/lb · Embodied Carbon (primary production) 3,100 kg CO₂/kg · Embodied Water 120,000 L/kg14,379 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PdNi-F vs PdNi-H02 — frequently asked
Is PdNi-H02 stronger than PdNi-F?
Yes. PdNi-H02 has a typical yield strength of 600 MPa (87 ksi) against 220 MPa (31.9 ksi) for PdNi-F — about 173% more. Tensile strength is 750 MPa (109 ksi) vs 450 MPa (65.3 ksi).
Which condition does FabDigit quote by default, F or H02?
M is the default PdNi condition in the FabDigit quote flow (neither F nor H02). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, PdNi-F or PdNi-H02?
PdNi-H02. Its machinability rates fair (35/100) against poor (25/100) for PdNi-F.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PdNi-F and PdNi-H02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.