Precious Metal AgC10 vs B780
Precious Metal · grade comparison
Precious Metal AgC10 and B780 are both precious metal grades. B780 is the stronger of the two: yield strength 125 MPa (18.1 ksi) against 70 MPa (10.2 ksi) for AgC10, about 79% more; tensile strength follows at 310 MPa (45 ksi) vs 110 MPa (16 ksi). B780 is the more ductile: elongation 30% versus 4% for AgC10, and B780 is harder (68 HB vs 30 HB). AgC10 is lighter (7.6 g/cm³ vs 10.05 g/cm³ for B780) and B780 is stiffer (88 GPa vs 55 GPa). On the shop floor, B780 welds better (good vs poor).
AgC10Choose it when weight is the constraint, or when the part sees heat.
B780Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AgC10 vs B780: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Hardness, Brinell
Shear Modulus
Bulk Modulus
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Machinability Rating (AISI 1212 = 100 %)
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Embodied Water
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AgC10 | B780 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
AgC10 vs B780 — frequently asked
Is B780 stronger than AgC10?
Yes. B780 has a typical yield strength of 125 MPa (18.1 ksi) against 70 MPa (10.2 ksi) for AgC10 — about 79% more. Tensile strength is 310 MPa (45 ksi) vs 110 MPa (16 ksi).
Which is cheaper, AgC10 or B780?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, AgC10 or B780?
AgC10. Its machinability rates good (55/100) against fair (50/100) for B780; for welding the order is B780 first (good, 60/100) then AgC10 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in AgC10 and B780 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.