Precious Metal Ag145 vs BAg-13a
Precious Metal · grade comparison
Precious Metal Ag145 and BAg-13a are both precious metal grades. Ag145 is the stronger of the two: yield strength 340 MPa (49.3 ksi) against 210 MPa (30.5 ksi) for BAg-13a, about 62% more; tensile strength follows at 450 MPa (65.3 ksi) vs 420 MPa (60.9 ksi). Ag145 is lighter (9.1 g/cm³ vs 9.75 g/cm³ for BAg-13a) and BAg-13a is stiffer (95 GPa vs 85 GPa). On the shop floor, BAg-13a machines more easily (good vs fair).
Ag145Choose it when strength drives the design, or when weight is the constraint.
BAg-13aChoose it when the part sees heat, or when the part is machined in volume.
Ag145 vs BAg-13a: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Brinell
Hardness, Vickers
Same in both: Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Castability
Brazeability / Solderability
Polishability
Same in both: Weldability 20 / 100 · Formability (cold) 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 29
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Ag145 | BAg-13a |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Ag145 vs BAg-13a — frequently asked
Is Ag145 stronger than BAg-13a?
Yes. Ag145 has a typical yield strength of 340 MPa (49.3 ksi) against 210 MPa (30.5 ksi) for BAg-13a — about 62% more. Tensile strength is 450 MPa (65.3 ksi) vs 420 MPa (60.9 ksi).
Which is cheaper, Ag145 or BAg-13a?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Ag145 or BAg-13a?
BAg-13a. Its machinability rates good (55/100) against fair (45/100) for Ag145.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Ag145 and BAg-13a side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.