Precious Metal 90Pt-10Ir vs AgC10
Precious Metal · grade comparison
Precious Metal 90Pt-10Ir and AgC10 are both precious metal grades. 90Pt-10Ir is the stronger of the two: yield strength 205 MPa (29.7 ksi) against 70 MPa (10.2 ksi) for AgC10, about 193% more; tensile strength follows at 415 MPa (60.2 ksi) vs 110 MPa (16 ksi). 90Pt-10Ir is the more ductile: elongation 28% versus 4% for AgC10, and 90Pt-10Ir is harder (125 HB vs 30 HB). AgC10 is lighter (7.6 g/cm³ vs 21.55 g/cm³ for 90Pt-10Ir) and 90Pt-10Ir is stiffer (190 GPa vs 55 GPa). On the shop floor, AgC10 machines more easily (good vs poor) and 90Pt-10Ir welds better (very good vs poor).
90Pt-10IrChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AgC10Choose it when weight is the constraint, or when the part is machined in volume.
90Pt-10Ir vs AgC10: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Compressive Strength
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 90Pt-10Ir | AgC10 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
90Pt-10Ir vs AgC10 — frequently asked
Is 90Pt-10Ir stronger than AgC10?
Yes. 90Pt-10Ir has a typical yield strength of 205 MPa (29.7 ksi) against 70 MPa (10.2 ksi) for AgC10 — about 193% more. Tensile strength is 415 MPa (60.2 ksi) vs 110 MPa (16 ksi).
Which is cheaper, 90Pt-10Ir or AgC10?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 90Pt-10Ir or AgC10?
AgC10. Its machinability rates good (55/100) against poor (30/100) for 90Pt-10Ir; for welding the order is 90Pt-10Ir first (very good, 70/100) then AgC10 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 90Pt-10Ir and AgC10 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.