Meldin 7001 vs Ultem 1000
Polymer · grade comparison
Meldin 7001 and Ultem 1000 are both polymer grades. Ultem 1000 is the stronger of the two: tensile strength 105 MPa (15.2 ksi) against 86 MPa (12.5 ksi) for Meldin 7001, about 22% more. Ultem 1000 is the more ductile: elongation 60% versus 7.5% for Meldin 7001. Ultem 1000 is lighter (1.27 g/cm³ vs 1.43 g/cm³ for Meldin 7001) and Meldin 7001 runs hotter in service (300°C vs 170°C continuous). On the shop floor, Ultem 1000 welds better (good vs not recommended).
Meldin 7001Choose it when the part sees heat.
Ultem 1000Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Meldin 7001 vs Ultem 1000: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Same in both: Compressive Modulus 2.9 GPa0.42 Msi · Hardness, Rockwell R 125 HRR
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Refractive Index
Light Transmission
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Limiting Oxygen Index
Max Service Temperature (short-term)
Vicat Softening Point (B50)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Surface Resistivity
Comparative Tracking Index (CTI)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
UV / Weathering Resistance
Same in both: Corrosion Resistance 85 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Polishability
Mold Shrinkage
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Same in both: Thermal Diffusivity 0.2 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Meldin 7001 | Ultem 1000 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Meldin 7001 vs Ultem 1000 — frequently asked
Is Ultem 1000 stronger than Meldin 7001?
Yes. Ultem 1000 has a typical tensile strength of 105 MPa (15.2 ksi) against 86 MPa (12.5 ksi) for Meldin 7001 — about 22% more.
Which is cheaper, Meldin 7001 or Ultem 1000?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Meldin 7001 or Ultem 1000?
Ultem 1000, by a small margin. Both rate good for machinability — 65/100 against 60/100 for Meldin 7001; for welding the order is Ultem 1000 first (good, 60/100) then Meldin 7001 (not recommended, 0/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Meldin 7001 and Ultem 1000 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.