EPS 150 vs XPS 700
Polymer · grade comparison
EPS 150 and XPS 700 are both polymer grades. XPS 700 is the stronger of the two: tensile strength 0.65 MPa (0.0943 ksi) against 0.3 MPa (0.0435 ksi) for EPS 150, about 117% more. XPS 700 is the more ductile: elongation 3% versus 2% for EPS 150. EPS 150 is lighter (0.03 g/cm³ vs 0.05 g/cm³ for XPS 700) and XPS 700 is stiffer (0.03 GPa vs 0.01 GPa). On the shop floor, EPS 150 welds better (fair vs poor).
EPS 150Choose it when weight is the constraint, or when it will be welded.
XPS 700Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
EPS 150 vs XPS 700: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Compression Set (22 h, 70 °C)
Physical
Density and transition temperatures.
Density
Water Absorption (24 h)
Water Absorption (Saturation)
Same in both: Glass Transition (Tg) 100°C212 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Specific Heat Capacity 1,400 J/kg·K0.33 BTU/lb·°F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Mold Shrinkage
Processing Melt Temperature (typ.)
Same in both: Formability (cold) 25 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | EPS 150 | XPS 700 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
EPS 150 vs XPS 700 — frequently asked
Is XPS 700 stronger than EPS 150?
Yes. XPS 700 has a typical tensile strength of 0.65 MPa (0.0943 ksi) against 0.3 MPa (0.0435 ksi) for EPS 150 — about 117% more.
Which is cheaper, EPS 150 or XPS 700?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, EPS 150 or XPS 700?
EPS 150. Its weldability rates fair (40/100) against poor (20/100) for XPS 700.
Ready to make it?
Upload a CAD file and FabDigit prices the part in EPS 150 and XPS 700 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.