Durus vs VeroBlackPlus
Polymer · grade comparison
Durus and VeroBlackPlus are both polymer grades. VeroBlackPlus is the stronger of the two: yield strength 50 MPa (7.25 ksi) against 22 MPa (3.19 ksi) for Durus, about 127% more; tensile strength follows at 55 MPa (7.98 ksi) vs 25 MPa (3.63 ksi). In exchange, Durus is the more ductile: elongation 45% versus 17% for VeroBlackPlus, and VeroBlackPlus is harder (84 Shore D vs 68 Shore D). VeroBlackPlus is stiffer (2.5 GPa vs 1.1 GPa). On the shop floor, VeroBlackPlus machines more easily (good vs fair).
DurusChoose it when the part is bent, formed or impact-loaded.
VeroBlackPlusChoose it when strength drives the design, or when the part is machined in volume.
Durus vs VeroBlackPlus: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell R
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Rockwell M
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Thermal Conductivity 0.2 W/m·K0.12 BTU/hr·ft·°F · Specific Heat Capacity 1,500 J/kg·K0.36 BTU/lb·°F · Max Service Temperature (continuous) 45°C113 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Volume Resistivity 1×10¹⁴ Ω·cm
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
UV / Weathering Resistance
Same in both: Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Same in both: Embodied Carbon (primary production) 5.5 kg CO₂/kg · Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Durus | VeroBlackPlus |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Durus vs VeroBlackPlus — frequently asked
Is VeroBlackPlus stronger than Durus?
Yes. VeroBlackPlus has a typical yield strength of 50 MPa (7.25 ksi) against 22 MPa (3.19 ksi) for Durus — about 127% more. Tensile strength is 55 MPa (7.98 ksi) vs 25 MPa (3.63 ksi).
Which is cheaper, Durus or VeroBlackPlus?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Durus or VeroBlackPlus?
VeroBlackPlus. Its machinability rates good (55/100) against fair (45/100) for Durus; for welding the order is VeroBlackPlus first (not recommended, 10/100) then Durus (not recommended, 5/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Durus and VeroBlackPlus side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.