C578 Type VII vs XPS 300
Polymer · grade comparison
C578 Type VII and XPS 300 are both polymer grades. C578 Type VII is the stronger of the two: tensile strength 0.55 MPa (0.0798 ksi) against 0.45 MPa (0.0653 ksi) for XPS 300, about 22% more. C578 Type VII is stiffer (0.02 GPa vs 0.02 GPa) and XPS 300 conducts heat better (0.03 W/m·K vs 0.03 W/m·K). On the shop floor, C578 Type VII forms better (poor vs not recommended).
C578 Type VIIChoose it when strength drives the design.
C578 Type VII vs XPS 300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Compressive Strength
Compressive Modulus
Flexural Strength
Shear Strength
Yield Strength (0.2% offset)
Elongation at Break
Flexural Modulus
Same in both: Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Density
Water Absorption (24 h)
Same in both: Glass Transition (Tg) 100°C212 °F · Water Absorption (Saturation) 0.5%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Min Service Temperature
Limiting Oxygen Index
Vicat Softening Point (B50)
Same in both: Specific Heat Capacity 1,450 J/kg·K0.35 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 70 µm/m·K38.9 µin/in·°F · Max Service Temperature (continuous) 75°C167 °F · Max Service Temperature (short-term) 85°C185 °F
Electrical
Conductivity and insulation.
Dielectric Constant (1 MHz)
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 15 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Processing Melt Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C578 Type VII | XPS 300 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
C578 Type VII vs XPS 300 — frequently asked
Is C578 Type VII stronger than XPS 300?
Yes. C578 Type VII has a typical tensile strength of 0.55 MPa (0.0798 ksi) against 0.45 MPa (0.0653 ksi) for XPS 300 — about 22% more.
Which is cheaper, C578 Type VII or XPS 300?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C578 Type VII or XPS 300?
XPS 300, by a small margin. Both rate excellent for machinability — 92/100 against 85/100 for C578 Type VII; for welding the order is C578 Type VII first (poor, 20/100) then XPS 300 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C578 Type VII and XPS 300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.