Nickel Alloy N08221-ANN vs N08221-AW
Nickel Alloy · N08221 temper comparison
N08221-ANN and N08221-AW are two conditions of the same nickel alloy grade, N08221: ANN (annealed) versus AW (as-welded deposit). The chemistry is identical, so every difference below comes from the condition. N08221-AW is the stronger of the two: yield strength 340 MPa (49.3 ksi) against 300 MPa (43.5 ksi) for N08221-ANN, about 13% more. In exchange, N08221-ANN is the more ductile: elongation 48% versus 35% for N08221-AW, and N08221-AW is harder (190 HB vs 170 HB). N08221-ANN runs hotter in service (500°C vs 450°C continuous).
N08221-ANNChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
N08221-AWChoose it when strength drives the design.
N08221-ANN vs N08221-AW: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.31
Physical
Density and transition temperatures.
Same in both: Density 8.1 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,330°C2,426 °F · Liquidus Temperature 1,385°C2,525 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 11 W/m·K6.4 BTU/hr·ft·°F · Specific Heat Capacity 450 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13.6 µm/m·K7.6 µin/in·°F · Latent Heat of Fusion 285 J/g123 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 78 / 100 · Castability 40 / 100 · Brazeability / Solderability 60 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 155 MJ/kg66,638 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
N08221-ANN vs N08221-AW — frequently asked
Is N08221-AW stronger than N08221-ANN?
Yes. N08221-AW has a typical yield strength of 340 MPa (49.3 ksi) against 300 MPa (43.5 ksi) for N08221-ANN — about 13% more. Tensile strength is 640 MPa (92.8 ksi) vs 650 MPa (94.3 ksi).
Which condition does FabDigit quote by default, ANN or AW?
ANN is the default N08221 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose N08221-ANN over N08221-AW?
Pick N08221-ANN when the part is bent, formed or impact-loaded, or when the part sees heat. Pick N08221-AW when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in N08221-ANN and N08221-AW side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.