Nickel Alloy Incoloy 800H vs Inconel 625
Nickel Alloy · grade comparison
Nickel Alloy Incoloy 800H and Inconel 625 are both nickel alloy grades. Inconel 625 is the stronger of the two: yield strength 490 MPa (71.1 ksi) against 220 MPa (31.9 ksi) for Incoloy 800H, about 123% more; tensile strength follows at 930 MPa (135 ksi) vs 520 MPa (75.4 ksi). Inconel 625 is harder — 190 HB against 140 HB for Incoloy 800H — which matters for wear surfaces and threads. Incoloy 800H is lighter (7.94 g/cm³ vs 8.44 g/cm³ for Inconel 625) and Inconel 625 is stiffer (207.5 GPa vs 196 GPa). On the shop floor, Incoloy 800H machines more easily (30 vs 18 out of 100) and Inconel 625 sits in a lower cost tier (premium, $$$) than Incoloy 800H (high, $$$$).
Incoloy 800HChoose it when weight is the constraint, or when the part sees heat.
Inconel 625Choose it when strength drives the design, or when surface hardness matters.
Incoloy 800H vs Inconel 625: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Same in both: Elongation at Break 45% · Reduction in Area 55%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 35%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Incoloy 800H | Inconel 625 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| 3D printing | — | Yes |
| Default condition | — | O |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | 1.5 mm |
| Best machined surface | — | Ra 1.6 µm |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
They share 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Incoloy 800H vs Inconel 625 — frequently asked
Is Inconel 625 stronger than Incoloy 800H?
Yes. Inconel 625 has a typical yield strength of 490 MPa (71.1 ksi) against 220 MPa (31.9 ksi) for Incoloy 800H — about 123% more. Tensile strength is 930 MPa (135 ksi) vs 520 MPa (75.4 ksi).
Which is cheaper, Incoloy 800H or Inconel 625?
Inconel 625 is the lower-cost material: it sits in the premium tier ($$$) while Incoloy 800H is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Incoloy 800H or Inconel 625?
Incoloy 800H, by a small margin. Both rate poor for machinability — 30/100 against 18/100 for Inconel 625; for welding the order is Inconel 625 first (excellent, 88/100) then Incoloy 800H (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Incoloy 800H and Inconel 625 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.