Nickel Alloy Hastelloy W-CD vs Hastelloy W HR-A
Nickel Alloy · Hastelloy W temper comparison
Hastelloy W-CD and Hastelloy W HR-A are two conditions of the same nickel alloy grade, Hastelloy W: CD (cold drawn) versus HR-A (hot worked and solution annealed). The chemistry is identical, so every difference below comes from the condition. Hastelloy W-CD is the stronger of the two: yield strength 880 MPa (128 ksi) against 380 MPa (55.1 ksi) for Hastelloy W HR-A, about 132% more; tensile strength follows at 1,100 MPa (160 ksi) vs 820 MPa (119 ksi). In exchange, Hastelloy W HR-A is the more ductile: elongation 42% versus 15% for Hastelloy W-CD, and Hastelloy W-CD is harder (300 HB vs 185 HB). Hastelloy W HR-A runs hotter in service (760°C vs 540°C continuous).
Hastelloy W-CDChoose it when strength drives the design.
Hastelloy W HR-AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Hastelloy W-CD vs Hastelloy W HR-A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Hastelloy W-CDHastelloy W HR-A
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 216 GPa31.3 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 190 GPa27.6 Msi · Poisson's Ratio 0.31
Physical
Density and transition temperatures.
Same in both: Density 9.03 g/cm³0.33 lb/in³ · Melting Point (Solidus) 1,305°C2,381 °F · Liquidus Temperature 1,370°C2,498 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 8.7 W/m·K5 BTU/hr·ft·°F · Specific Heat Capacity 375 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.3 µm/m·K6.3 µin/in·°F · Latent Heat of Fusion 290 J/g125 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 60 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Hastelloy W-CD vs Hastelloy W HR-A — frequently asked
Is Hastelloy W-CD stronger than Hastelloy W HR-A?
Yes. Hastelloy W-CD has a typical yield strength of 880 MPa (128 ksi) against 380 MPa (55.1 ksi) for Hastelloy W HR-A — about 132% more. Tensile strength is 1,100 MPa (160 ksi) vs 820 MPa (119 ksi).
Which condition does FabDigit quote by default, CD or HR-A?
SA is the default Hastelloy W condition in the FabDigit quote flow (neither CD nor HR-A). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Hastelloy W-CD or Hastelloy W HR-A?
Hastelloy W HR-A. Its weldability rates very good (80/100) against very good (72/100) for Hastelloy W-CD.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Hastelloy W-CD and Hastelloy W HR-A side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.