Nickel Alloy Hastelloy N Cast vs Hastelloy N-CW
Nickel Alloy · Hastelloy N temper comparison
Hastelloy N Cast and Hastelloy N-CW are two conditions of the same nickel alloy grade, Hastelloy N: Cast (as cast) versus CW (cold worked). The chemistry is identical, so every difference below comes from the condition. Hastelloy N-CW is the stronger of the two: yield strength 800 MPa (116 ksi) against 300 MPa (43.5 ksi) for Hastelloy N Cast, about 167% more; tensile strength follows at 1,030 MPa (149 ksi) vs 550 MPa (79.8 ksi). Hastelloy N-CW is harder — 285 HB against 200 HB for Hastelloy N Cast — which matters for wear surfaces and threads. Hastelloy N Cast runs hotter in service (704°C vs 540°C continuous). On the shop floor, Hastelloy N-CW forms better (poor vs not recommended).
Hastelloy N CastChoose it when the part sees heat.
Hastelloy N-CWChoose it when strength drives the design, or when surface hardness matters.
Hastelloy N Cast vs Hastelloy N-CW: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Hastelloy N CastHastelloy N-CW
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 180 GPa26.1 Msi · Poisson's Ratio 0.31 · Elongation at Break 15%
Physical
Density and transition temperatures.
Same in both: Density 8.86 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,300°C2,372 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 290 J/g125 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 80 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 60 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 165 MJ/kg70,937 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 220 L/kg26.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Hastelloy N Cast vs Hastelloy N-CW — frequently asked
Is Hastelloy N-CW stronger than Hastelloy N Cast?
Yes. Hastelloy N-CW has a typical yield strength of 800 MPa (116 ksi) against 300 MPa (43.5 ksi) for Hastelloy N Cast — about 167% more. Tensile strength is 1,030 MPa (149 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, Cast or CW?
SA is the default Hastelloy N condition in the FabDigit quote flow (neither Cast nor CW). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, Hastelloy N Cast or Hastelloy N-CW?
Hastelloy N-CW, by a small margin. Both rate poor for machinability — 24/100 against 15/100 for Hastelloy N Cast; for welding the order is Hastelloy N-CW first (very good, 70/100) then Hastelloy N Cast (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Hastelloy N Cast and Hastelloy N-CW side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.