Nickel Alloy CZ-100 vs K417G
Nickel Alloy · grade comparison
Nickel Alloy CZ-100 and K417G are both nickel alloy grades. K417G is the stronger of the two: yield strength 800 MPa (116 ksi) against 160 MPa (23.2 ksi) for CZ-100, about 5.0 times as much; tensile strength follows at 920 MPa (133 ksi) vs 380 MPa (55.1 ksi). In exchange, CZ-100 is the more ductile: elongation 25% versus 6% for K417G, and K417G is harder (345 HB vs 110 HB). K417G is lighter (7.8 g/cm³ vs 8.85 g/cm³ for CZ-100) and K417G is stiffer (205 GPa vs 180 GPa). On the shop floor, CZ-100 machines more easily (fair vs not recommended) and CZ-100 welds better (good vs not recommended).
CZ-100Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
K417GChoose it when strength drives the design, or when weight is the constraint.
CZ-100 vs K417G: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Fracture Toughness (K_IC)
Hardness, Rockwell C
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | CZ-100 | K417G |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
CZ-100 vs K417G — frequently asked
Is K417G stronger than CZ-100?
Yes. K417G has a typical yield strength of 800 MPa (116 ksi) against 160 MPa (23.2 ksi) for CZ-100 — about 5.0 times as much. Tensile strength is 920 MPa (133 ksi) vs 380 MPa (55.1 ksi).
Which is cheaper, CZ-100 or K417G?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, CZ-100 or K417G?
CZ-100. Its machinability rates fair (35/100) against not recommended (10/100) for K417G; for welding the order is CZ-100 first (good, 60/100) then K417G (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in CZ-100 and K417G side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.