Beech vs Oak
Natural Material · grade comparison
Beech and Oak are both natural material grades. Beech is the stronger of the two: tensile strength 110 MPa (16 ksi) against 95 MPa (13.8 ksi) for Oak, about 16% more. Beech is the more ductile: elongation 1.2% versus 1% for Oak. Beech is stiffer (14 GPa vs 12.3 GPa) and Beech runs hotter in service (100°C vs 90°C continuous). On the shop floor, Beech sits in a lower cost tier (budget, $) than Oak (standard, $$).
BeechChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Beech vs Oak: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all natural material grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all natural material grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Hardness, Mohs
Same in both: Shear Modulus 1.1 GPa0.16 Msi · Fracture Toughness (K_IC) 0.5 MPa·√m0.46 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 0.72 g/cm³0.03 lb/in³ · Porosity 52%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹⁰ Ω·m3.94×10¹⁷ µΩ·in · Dielectric Strength 4 kV/mm102 V/mil
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Polishability
Same in both: Machinability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Same in both: Embodied Energy (primary production) 11 MJ/kg4,729 BTU/lb · Typical Recycled Content 5%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every natural material grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Beech | Oak |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Beech vs Oak — frequently asked
Is Beech stronger than Oak?
Yes. Beech has a typical tensile strength of 110 MPa (16 ksi) against 95 MPa (13.8 ksi) for Oak — about 16% more.
Which is cheaper, Beech or Oak?
Beech is the lower-cost material: it sits in the budget tier ($) while Oak is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose Beech over Oak?
Pick Beech when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Beech and Oak side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.