Magnesium Alloy AM60B vs ZC63
Magnesium Alloy · grade comparison
Magnesium Alloy AM60B and ZC63 are both magnesium alloy grades. ZC63 is the stronger of the two: yield strength 145 MPa (21 ksi) against 130 MPa (18.9 ksi) for AM60B, about 12% more; tensile strength follows at 240 MPa (34.8 ksi) vs 225 MPa (32.6 ksi). In exchange, AM60B is the more ductile: elongation 8% versus 5% for ZC63. AM60B is lighter (1.8 g/cm³ vs 1.87 g/cm³ for ZC63) and ZC63 conducts heat better (122 W/m·K vs 61 W/m·K). On the shop floor, AM60B sits in a lower cost tier (standard, $$) than ZC63 (premium, $$$).
AM60BChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
ZC63Choose it when strength drives the design.
AM60B vs ZC63: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Same in both: Elastic (Young's) Modulus 45 GPa6.5 Msi · Shear Modulus 17 GPa2.5 Msi · Bulk Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.35 · Shear Strength 140 MPa20.3 ksi · Hardness, Brinell 62 HB
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 120°C248 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Same in both: Machinability 95 / 100 · Brazeability / Solderability 20 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 500 L/kg59.9 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AM60B | ZC63 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | As Cast | — |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Chem Film (Alodine) | Yes | — |
| E-Coating | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
AM60B vs ZC63 — frequently asked
Is ZC63 stronger than AM60B?
Yes. ZC63 has a typical yield strength of 145 MPa (21 ksi) against 130 MPa (18.9 ksi) for AM60B — about 12% more. Tensile strength is 240 MPa (34.8 ksi) vs 225 MPa (32.6 ksi).
Which is cheaper, AM60B or ZC63?
AM60B is the lower-cost material: it sits in the standard tier ($$) while ZC63 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, AM60B or ZC63?
AM60B. Its weldability rates fair (40/100) against fair (35/100) for ZC63.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AM60B and ZC63 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.