Copper Alloy TP2-H01 vs TP2-M20
Copper Alloy · TP2 temper comparison
TP2-H01 and TP2-M20 are two conditions of the same copper alloy grade, TP2: H01 (quarter hard) versus M20 (as hot rolled). The chemistry is identical, so every difference below comes from the condition. TP2-H01 is the stronger of the two: yield strength 205 MPa (29.7 ksi) against 75 MPa (10.9 ksi) for TP2-M20, about 173% more; tensile strength follows at 265 MPa (38.4 ksi) vs 220 MPa (31.9 ksi). In exchange, TP2-M20 is the more ductile: elongation 40% versus 25% for TP2-H01, and TP2-H01 is harder (75 HB vs 45 HB).
TP2-H01Choose it when strength drives the design.
TP2-M20Choose it when the part is bent, formed or impact-loaded.
TP2-H01 vs TP2-M20: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,083°C1,981 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 339 W/m·K196 BTU/hr·ft·°F · Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 85 % IACS · Electrical Resistivity 2.03×10⁻⁸ Ω·m0.799 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Castability 45 / 100 · Brazeability / Solderability 98 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 330 L/kg39.5 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
TP2-H01 vs TP2-M20 — frequently asked
Is TP2-H01 stronger than TP2-M20?
Yes. TP2-H01 has a typical yield strength of 205 MPa (29.7 ksi) against 75 MPa (10.9 ksi) for TP2-M20 — about 173% more. Tensile strength is 265 MPa (38.4 ksi) vs 220 MPa (31.9 ksi).
Which condition does FabDigit quote by default, H01 or M20?
H58 is the default TP2 condition in the FabDigit quote flow (neither H01 nor M20). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, TP2-H01 or TP2-M20?
TP2-H01, by a small margin. Both rate poor for machinability — 25/100 against 20/100 for TP2-M20; for welding the order is TP2-M20 first (excellent, 85/100) then TP2-H01 (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in TP2-H01 and TP2-M20 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.