Copper Alloy C84400 vs CC333G
Copper Alloy · grade comparison
Copper Alloy C84400 and CC333G are both copper alloy grades. CC333G is the stronger of the two: yield strength 270 MPa (39.2 ksi) against 110 MPa (16 ksi) for C84400, about 145% more; tensile strength follows at 650 MPa (94.3 ksi) vs 234 MPa (33.9 ksi). In exchange, C84400 is the more ductile: elongation 26% versus 18% for CC333G, and CC333G is harder (160 HB vs 55 HB). CC333G is lighter (7.6 g/cm³ vs 8.8 g/cm³ for C84400) and CC333G is stiffer (117 GPa vs 95 GPa). On the shop floor, C84400 machines more easily (excellent vs fair), CC333G welds better (very good vs poor), and CC333G sits in a lower cost tier (high, $$$$) than C84400 (specialty, $$$$$).
C84400Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
CC333GChoose it when strength drives the design, or when weight is the constraint.
C84400 vs CC333G: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Reduction in Area
Fracture Toughness (K_IC)
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C84400 | CC333G |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | As Cast | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C84400 vs CC333G — frequently asked
Is CC333G stronger than C84400?
Yes. CC333G has a typical yield strength of 270 MPa (39.2 ksi) against 110 MPa (16 ksi) for C84400 — about 145% more. Tensile strength is 650 MPa (94.3 ksi) vs 234 MPa (33.9 ksi).
Which is cheaper, C84400 or CC333G?
CC333G is the lower-cost material: it sits in the high tier ($$$$) while C84400 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C84400 or CC333G?
C84400. Its machinability rates excellent (90/100) against fair (35/100) for CC333G; for welding the order is CC333G first (very good, 70/100) then C84400 (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C84400 and CC333G side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.