Copper Alloy C84200-M02 vs C84200-M06
Copper Alloy · C84200 temper comparison
C84200-M02 and C84200-M06 are two conditions of the same copper alloy grade, C84200: M02 (as centrifugally cast) versus M06 (as investment cast). The chemistry is identical, so every difference below comes from the condition. C84200-M02 is the stronger of the two: yield strength 110 MPa (16 ksi) against 103 MPa (14.9 ksi) for C84200-M06, about 7% more; tensile strength follows at 255 MPa (37 ksi) vs 241 MPa (35 ksi). C84200-M02 is harder — 58 HB against 55 HB for C84200-M06 — which matters for wear surfaces and threads.
C84200-M02Choose it when strength drives the design, or when surface hardness matters.
C84200-M02 vs C84200-M06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 95 GPa13.8 Msi · Shear Modulus 36 GPa5.2 Msi · Bulk Modulus 100 GPa14.5 Msi · Poisson's Ratio 0.34 · Elongation at Break 25%
Physical
Density and transition temperatures.
Same in both: Density 8.6 g/cm³0.31 lb/in³ · Melting Point (Solidus) 843°C1,549 °F · Liquidus Temperature 1,004°C1,839 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 72 W/m·K41.6 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18 µm/m·K10 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 16.4 % IACS · Electrical Resistivity 1.05×10⁻⁷ Ω·m4.13 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 80 / 100 · Machinability Rating (AISI 1212 = 100 %) 80% · Weldability 20 / 100 · Formability (cold) 15 / 100 · Castability 85 / 100 · Brazeability / Solderability 80 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C84200-M02 vs C84200-M06 — frequently asked
Is C84200-M02 stronger than C84200-M06?
Yes. C84200-M02 has a typical yield strength of 110 MPa (16 ksi) against 103 MPa (14.9 ksi) for C84200-M06 — about 7% more. Tensile strength is 255 MPa (37 ksi) vs 241 MPa (35 ksi).
Which condition does FabDigit quote by default, M02 or M06?
M01 is the default C84200 condition in the FabDigit quote flow (neither M02 nor M06). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C84200-M02 over C84200-M06?
Pick C84200-M02 when strength drives the design, or when surface hardness matters.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C84200-M02 and C84200-M06 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.