Copper Alloy C83400 vs ZCuZn33Pb2
Copper Alloy · grade comparison
Copper Alloy C83400 and ZCuZn33Pb2 are both copper alloy grades. ZCuZn33Pb2 is the stronger of the two: yield strength 80 MPa (11.6 ksi) against 69 MPa (10 ksi) for C83400, about 16% more. In exchange, C83400 is the more ductile: elongation 35% versus 18% for ZCuZn33Pb2, and ZCuZn33Pb2 is harder (55 HB vs 50 HB). ZCuZn33Pb2 is lighter (8.5 g/cm³ vs 8.8 g/cm³ for C83400) and C83400 is stiffer (96.5 GPa vs 90 GPa). On the shop floor, ZCuZn33Pb2 machines more easily (excellent vs good), C83400 welds better (fair vs poor), and ZCuZn33Pb2 sits in a lower cost tier (premium, $$$) than C83400 (high, $$$$).
C83400Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
ZCuZn33Pb2Choose it when strength drives the design, or when weight is the constraint.
C83400 vs ZCuZn33Pb2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Compressive Strength
Hardness, Rockwell B
Same in both: Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Formability (cold) 30 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C83400 | ZCuZn33Pb2 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | As Cast | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C83400 vs ZCuZn33Pb2 — frequently asked
Is ZCuZn33Pb2 stronger than C83400?
Yes. ZCuZn33Pb2 has a typical yield strength of 80 MPa (11.6 ksi) against 69 MPa (10 ksi) for C83400 — about 16% more. Tensile strength is 200 MPa (29 ksi) vs 234 MPa (33.9 ksi).
Which is cheaper, C83400 or ZCuZn33Pb2?
ZCuZn33Pb2 is the lower-cost material: it sits in the premium tier ($$$) while C83400 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C83400 or ZCuZn33Pb2?
ZCuZn33Pb2. Its machinability rates excellent (85/100) against good (58/100) for C83400; for welding the order is C83400 first (fair, 45/100) then ZCuZn33Pb2 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C83400 and ZCuZn33Pb2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.