Copper Alloy C77400-H01 vs C77400-H06
Copper Alloy · C77400 temper comparison
C77400-H01 and C77400-H06 are two conditions of the same copper alloy grade, C77400: H01 (quarter hard) versus H06 (extra hard). The chemistry is identical, so every difference below comes from the condition. C77400-H06 is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 340 MPa (49.3 ksi) for C77400-H01, about 82% more; tensile strength follows at 690 MPa (100 ksi) vs 460 MPa (66.7 ksi). In exchange, C77400-H01 is the more ductile: elongation 20% versus 2% for C77400-H06, and C77400-H06 is harder (195 HB vs 125 HB). C77400-H01 runs hotter in service (200°C vs 175°C continuous).
C77400-H01Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C77400-H06Choose it when strength drives the design.
C77400-H01 vs C77400-H06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 125 GPa18.1 Msi · Shear Modulus 47 GPa6.8 Msi · Bulk Modulus 122 GPa17.7 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.7 g/cm³0.31 lb/in³ · Melting Point (Solidus) 960°C1,760 °F · Liquidus Temperature 1,010°C1,850 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 45 W/m·K26 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 11 % IACS · Electrical Resistivity 1.57×10⁻⁷ Ω·m6.18 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 85 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60 MJ/kg25,795 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C77400-H01 vs C77400-H06 — frequently asked
Is C77400-H06 stronger than C77400-H01?
Yes. C77400-H06 has a typical yield strength of 620 MPa (89.9 ksi) against 340 MPa (49.3 ksi) for C77400-H01 — about 82% more. Tensile strength is 690 MPa (100 ksi) vs 460 MPa (66.7 ksi).
Which condition does FabDigit quote by default, H01 or H06?
H02 is the default C77400 condition in the FabDigit quote flow (neither H01 nor H06). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C77400-H01 or C77400-H06?
C77400-H06, by a small margin. Both rate poor for machinability — 30/100 against 25/100 for C77400-H01; for welding the order is C77400-H01 first (fair, 50/100) then C77400-H06 (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C77400-H01 and C77400-H06 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.