Copper Alloy C74500-H02 vs C74500-H10
Copper Alloy · C74500 temper comparison
C74500-H02 and C74500-H10 are two conditions of the same copper alloy grade, C74500: H02 (half hard) versus H10 (extra spring hard). The chemistry is identical, so every difference below comes from the condition. C74500-H10 is the stronger of the two: yield strength 675 MPa (97.9 ksi) against 400 MPa (58 ksi) for C74500-H02, about 69% more; tensile strength follows at 725 MPa (105 ksi) vs 510 MPa (74 ksi). In exchange, C74500-H02 is the more ductile: elongation 12% versus 2% for C74500-H10, and C74500-H10 is harder (213 HB vs 150 HB). C74500-H02 runs hotter in service (180°C vs 140°C continuous).
C74500-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C74500-H10Choose it when strength drives the design.
C74500-H02 vs C74500-H10: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 127 GPa18.4 Msi · Shear Modulus 48 GPa7 Msi · Bulk Modulus 128 GPa18.6 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.73 g/cm³0.32 lb/in³ · Melting Point (Solidus) 954°C1,749 °F · Liquidus Temperature 1,021°C1,870 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 195 J/g83.8 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.26 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 88 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 5.2 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C74500-H02 vs C74500-H10 — frequently asked
Is C74500-H10 stronger than C74500-H02?
Yes. C74500-H10 has a typical yield strength of 675 MPa (97.9 ksi) against 400 MPa (58 ksi) for C74500-H02 — about 69% more. Tensile strength is 725 MPa (105 ksi) vs 510 MPa (74 ksi).
Which condition does FabDigit quote by default, H02 or H10?
H02 is the default C74500 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C74500-H02 or C74500-H10?
C74500-H10. Its machinability rates fair (35/100) against poor (30/100) for C74500-H02; for welding the order is C74500-H02 first (fair, 40/100) then C74500-H10 (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C74500-H02 and C74500-H10 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.