Copper Alloy C71700-H01 vs C71700-H04
Copper Alloy · C71700 temper comparison
C71700-H01 and C71700-H04 are two conditions of the same copper alloy grade, C71700: H01 (quarter hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. C71700-H04 is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 310 MPa (45 ksi) for C71700-H01, about 77% more; tensile strength follows at 620 MPa (89.9 ksi) vs 470 MPa (68.2 ksi). In exchange, C71700-H01 is the more ductile: elongation 22% versus 8% for C71700-H04, and C71700-H04 is harder (190 HB vs 125 HB). C71700-H01 runs hotter in service (350°C vs 300°C continuous).
C71700-H01Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C71700-H04Choose it when strength drives the design.
C71700-H01 vs C71700-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 152 GPa22 Msi · Shear Modulus 57 GPa8.3 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,170°C2,138 °F · Liquidus Temperature 1,240°C2,264 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 29 W/m·K16.8 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 220 J/g94.6 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 82 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 80 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 105 MJ/kg45,142 BTU/lb · Embodied Carbon (primary production) 7.5 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C71700-H01 vs C71700-H04 — frequently asked
Is C71700-H04 stronger than C71700-H01?
Yes. C71700-H04 has a typical yield strength of 550 MPa (79.8 ksi) against 310 MPa (45 ksi) for C71700-H01 — about 77% more. Tensile strength is 620 MPa (89.9 ksi) vs 470 MPa (68.2 ksi).
Which condition does FabDigit quote by default, H01 or H04?
O61 is the default C71700 condition in the FabDigit quote flow (neither H01 nor H04). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C71700-H01 or C71700-H04?
C71700-H04, by a small margin. Both rate poor for machinability — 30/100 against 24/100 for C71700-H01.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C71700-H01 and C71700-H04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.