Copper Alloy C71500-H01 vs C71500-H04
Copper Alloy · C71500 temper comparison
C71500-H01 and C71500-H04 are two conditions of the same copper alloy grade, C71500: H01 (quarter hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. C71500-H04 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 275 MPa (39.9 ksi) for C71500-H01, about 75% more; tensile strength follows at 515 MPa (74.7 ksi) vs 415 MPa (60.2 ksi). In exchange, C71500-H01 is the more ductile: elongation 25% versus 8% for C71500-H04, and C71500-H04 is harder (150 HB vs 110 HB). C71500-H01 runs hotter in service (250°C vs 200°C continuous). On the shop floor, C71500-H04 machines more easily (45 vs 35 out of 100).
C71500-H01Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C71500-H04Choose it when strength drives the design, or when the part is machined in volume.
C71500-H01 vs C71500-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 152 GPa22 Msi · Shear Modulus 57 GPa8.3 Msi · Bulk Modulus 158 GPa22.9 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,171°C2,140 °F · Liquidus Temperature 1,238°C2,260 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 29 W/m·K16.8 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 230 J/g98.9 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 80 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 110 MJ/kg47,292 BTU/lb · Embodied Carbon (primary production) 7 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C71500-H01 vs C71500-H04 — frequently asked
Is C71500-H04 stronger than C71500-H01?
Yes. C71500-H04 has a typical yield strength of 480 MPa (69.6 ksi) against 275 MPa (39.9 ksi) for C71500-H01 — about 75% more. Tensile strength is 515 MPa (74.7 ksi) vs 415 MPa (60.2 ksi).
Which condition does FabDigit quote by default, H01 or H04?
O61 is the default C71500 condition in the FabDigit quote flow (neither H01 nor H04). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C71500-H01 or C71500-H04?
C71500-H04, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for C71500-H01; for welding the order is C71500-H01 first (very good, 80/100) then C71500-H04 (very good, 75/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C71500-H01 and C71500-H04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.