Copper Alloy C69400-H02 vs C69400-M20
Copper Alloy · C69400 temper comparison
C69400-H02 and C69400-M20 are two conditions of the same copper alloy grade, C69400: H02 (half hard) versus M20 (as hot rolled). The chemistry is identical, so every difference below comes from the condition. C69400-H02 is the stronger of the two: yield strength 415 MPa (60.2 ksi) against 310 MPa (45 ksi) for C69400-M20, about 34% more; tensile strength follows at 655 MPa (95 ksi) vs 590 MPa (85.6 ksi). In exchange, C69400-M20 is the more ductile: elongation 25% versus 20% for C69400-H02, and C69400-H02 is harder (180 HB vs 155 HB). C69400-M20 runs hotter in service (200°C vs 175°C continuous).
C69400-H02Choose it when strength drives the design.
C69400-M20Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C69400-H02 vs C69400-M20: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 38 GPa5.5 Msi · Bulk Modulus 107 GPa15.5 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.3 g/cm³0.3 lb/in³ · Melting Point (Solidus) 820°C1,508 °F · Liquidus Temperature 917°C1,683 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.2 µm/m·K11.2 µin/in·°F · Latent Heat of Fusion 190 J/g81.7 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 66 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 75 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C69400-H02 vs C69400-M20 — frequently asked
Is C69400-H02 stronger than C69400-M20?
Yes. C69400-H02 has a typical yield strength of 415 MPa (60.2 ksi) against 310 MPa (45 ksi) for C69400-M20 — about 34% more. Tensile strength is 655 MPa (95 ksi) vs 590 MPa (85.6 ksi).
Which condition does FabDigit quote by default, H02 or M20?
M30 is the default C69400 condition in the FabDigit quote flow (neither H02 nor M20). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C69400-H02 over C69400-M20?
Pick C69400-H02 when strength drives the design. Pick C69400-M20 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C69400-H02 and C69400-M20 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.