Copper Alloy C51900 vs C67000
Copper Alloy · grade comparison
Copper Alloy C51900 and C67000 are both copper alloy grades. C51900 is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 379 MPa (55 ksi) for C67000, about 19% more. C67000 is harder — 185 HB against 155 HB for C51900 — which matters for wear surfaces and threads. C67000 is lighter (8.36 g/cm³ vs 8.8 g/cm³ for C51900) and C51900 is stiffer (115 GPa vs 103 GPa). On the shop floor, C51900 welds better (fair vs poor), C51900 forms better (good vs fair), and C67000 sits in a lower cost tier (high, $$$$) than C51900 (specialty, $$$$$).
C51900Choose it when strength drives the design, or when it will be welded.
C67000Choose it when surface hardness matters, or when weight is the constraint.
C51900 vs C67000: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Charpy V-Notch Impact (RT)
Same in both: Poisson's Ratio 0.34 · Elongation at Break 20% · Reduction in Area 35%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C51900 | C67000 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C51900 vs C67000 — frequently asked
Is C51900 stronger than C67000?
Yes. C51900 has a typical yield strength of 450 MPa (65.3 ksi) against 379 MPa (55 ksi) for C67000 — about 19% more. Tensile strength is 520 MPa (75.4 ksi) vs 655 MPa (95 ksi).
Which is cheaper, C51900 or C67000?
C67000 is the lower-cost material: it sits in the high tier ($$$$) while C51900 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C51900 or C67000?
C67000, by a small margin. Both rate poor for machinability — 32/100 against 25/100 for C51900; for welding the order is C51900 first (fair, 45/100) then C67000 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C51900 and C67000 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.