Copper Alloy C46200-H02 vs C46200-O60
Copper Alloy · C46200 temper comparison
C46200-H02 and C46200-O60 are two conditions of the same copper alloy grade, C46200: H02 (half hard) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. C46200-H02 is the stronger of the two: yield strength 360 MPa (52.2 ksi) against 170 MPa (24.7 ksi) for C46200-O60, about 112% more; tensile strength follows at 470 MPa (68.2 ksi) vs 385 MPa (55.8 ksi). In exchange, C46200-O60 is the more ductile: elongation 47% versus 20% for C46200-H02, and C46200-H02 is harder (150 HB vs 95 HB). C46200-O60 runs hotter in service (250°C vs 175°C continuous). On the shop floor, C46200-H02 machines more easily (50 vs 40 out of 100).
C46200-H02Choose it when strength drives the design, or when the part is machined in volume.
C46200-O60Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C46200-H02 vs C46200-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 100 GPa14.5 Msi · Shear Modulus 38 GPa5.5 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.41 g/cm³0.3 lb/in³ · Melting Point (Solidus) 885°C1,625 °F · Liquidus Temperature 900°C1,652 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 116 W/m·K67 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21.2 µm/m·K11.8 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 26 % IACS · Electrical Resistivity 6.6×10⁻⁸ Ω·m2.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Castability 55 / 100 · Brazeability / Solderability 90 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.9 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C46200-H02 vs C46200-O60 — frequently asked
Is C46200-H02 stronger than C46200-O60?
Yes. C46200-H02 has a typical yield strength of 360 MPa (52.2 ksi) against 170 MPa (24.7 ksi) for C46200-O60 — about 112% more. Tensile strength is 470 MPa (68.2 ksi) vs 385 MPa (55.8 ksi).
Which condition does FabDigit quote by default, H02 or O60?
M30 is the default C46200 condition in the FabDigit quote flow (neither H02 nor O60). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C46200-H02 or C46200-O60?
C46200-H02, by a small margin. Both rate fair for machinability — 50/100 against 40/100 for C46200-O60.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C46200-H02 and C46200-O60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.