Copper Alloy C33200-H04 vs C33200-H80
Copper Alloy · C33200 temper comparison
C33200-H04 and C33200-H80 are two conditions of the same copper alloy grade, C33200: H04 (full hard) versus H80 (hard drawn). The chemistry is identical, so every difference below comes from the condition. C33200-H80 is the stronger of the two: yield strength 415 MPa (60.2 ksi) against 370 MPa (53.7 ksi) for C33200-H04, about 12% more; tensile strength follows at 515 MPa (74.7 ksi) vs 470 MPa (68.2 ksi). In exchange, C33200-H04 is the more ductile: elongation 12% versus 7% for C33200-H80, and C33200-H80 is harder (140 HB vs 130 HB).
C33200-H04Choose it when the part is bent, formed or impact-loaded.
C33200-H80Choose it when strength drives the design.
C33200-H04 vs C33200-H80: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.47 g/cm³0.31 lb/in³ · Melting Point (Solidus) 899°C1,650 °F · Liquidus Temperature 932°C1,710 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 116 W/m·K67 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.2 µm/m·K11.2 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 26 % IACS · Electrical Resistivity 6.6×10⁻⁸ Ω·m2.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 82 / 100 · Weldability 20 / 100 · Brazeability / Solderability 88 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C33200-H04 vs C33200-H80 — frequently asked
Is C33200-H80 stronger than C33200-H04?
Yes. C33200-H80 has a typical yield strength of 415 MPa (60.2 ksi) against 370 MPa (53.7 ksi) for C33200-H04 — about 12% more. Tensile strength is 515 MPa (74.7 ksi) vs 470 MPa (68.2 ksi).
Which condition does FabDigit quote by default, H04 or H80?
H80 is the default C33200 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C33200-H04 over C33200-H80?
Pick C33200-H04 when the part is bent, formed or impact-loaded. Pick C33200-H80 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C33200-H04 and C33200-H80 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.