Copper Alloy C33000 vs C66300
Copper Alloy · grade comparison
Copper Alloy C33000 and C66300 are both copper alloy grades. C66300 is the stronger of the two: yield strength 600 MPa (87 ksi) against 110 MPa (16 ksi) for C33000, about 5.5 times as much; tensile strength follows at 660 MPa (95.7 ksi) vs 340 MPa (49.3 ksi). In exchange, C33000 is the more ductile: elongation 55% versus 3.5% for C66300, and C66300 is harder (195 HV vs 58 HV). C66300 is stiffer (110 GPa vs 103 GPa) and C33000 runs hotter in service (200°C vs 120°C continuous). On the shop floor, C33000 machines more easily (very good vs fair).
C33000Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C66300Choose it when strength drives the design.
C33000 vs C66300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 375 J/kg·K0.09 BTU/lb·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Same in both: Embodied Carbon (primary production) 3.6 kg CO₂/kg · Typical Recycled Content 50%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C33000 | C66300 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C33000 vs C66300 — frequently asked
Is C66300 stronger than C33000?
Yes. C66300 has a typical yield strength of 600 MPa (87 ksi) against 110 MPa (16 ksi) for C33000 — about 5.5 times as much. Tensile strength is 660 MPa (95.7 ksi) vs 340 MPa (49.3 ksi).
Which is cheaper, C33000 or C66300?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C33000 or C66300?
C33000. Its machinability rates very good (70/100) against fair (35/100) for C66300; for welding the order is C66300 first (poor, 30/100) then C33000 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C33000 and C66300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.