Copper Alloy C33000 vs C35600
Copper Alloy · grade comparison
Copper Alloy C33000 and C35600 are both copper alloy grades. C35600 is the stronger of the two: yield strength 340 MPa (49.3 ksi) against 110 MPa (16 ksi) for C33000, about 3.1 times as much; tensile strength follows at 425 MPa (61.6 ksi) vs 340 MPa (49.3 ksi). In exchange, C33000 is the more ductile: elongation 55% versus 15% for C35600, and C35600 is harder (125 HB vs 55 HB). C33000 is stiffer (103 GPa vs 97 GPa) and C33000 runs hotter in service (200°C vs 180°C continuous). On the shop floor, C35600 machines more easily (excellent vs very good) and C35600 sits in a lower cost tier (premium, $$$) than C33000 (high, $$$$).
C33000Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C35600Choose it when strength drives the design, or when the part is machined in volume.
C33000 vs C35600: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 8.47 g/cm³0.31 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 26 % IACS · Electrical Resistivity 6.6×10⁻⁸ Ω·m2.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Castability
Same in both: Brazeability / Solderability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 3.6 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C33000 | C35600 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C33000 vs C35600 — frequently asked
Is C35600 stronger than C33000?
Yes. C35600 has a typical yield strength of 340 MPa (49.3 ksi) against 110 MPa (16 ksi) for C33000 — about 3.1 times as much. Tensile strength is 425 MPa (61.6 ksi) vs 340 MPa (49.3 ksi).
Which is cheaper, C33000 or C35600?
C35600 is the lower-cost material: it sits in the premium tier ($$$) while C33000 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C33000 or C35600?
C35600. Its machinability rates excellent (100/100) against very good (70/100) for C33000; for welding the order is C33000 first (poor, 25/100) then C35600 (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C33000 and C35600 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.